Home  >  Info. center  >  Knowledge  >  The bending characteristics of 304 stainless steel plate

Knowledge

The bending characteristics of 304 stainless steel plate

2015/07/03

The bending characteristics of 304 stainless steel plate

    304 stainless steel surface appearance and the use of diverse possibilities, good corrosion resistance, long-term durability than ordinary steel, 304 stainless steel, good corrosion resistance, high strength, and therefore the possibility of the use of thin, high temperature oxidation and strength, it is possible to Anti-fire in room temperature, that is easy to plastic processing, surface treatment because you do not so simple, clean and simple maintenance, good finish high welding performance.

    316 and 304 the main difference in the chemical composition is the 316 Mo, but is generally accepted that the corrosion resistance of 316 better than the 304 more under high temperature corrosion resistance. Therefore, in a high temperature environment, engineers usually use 316 material parts. But things are no so-called absolute, in concentrated sulfuric acid environment, then do not use high temperature 316, we know that in order to prevent thread killed at high temperatures, you need to apply a dark solid lubricant.

    304 stainless steel itself since the high yield, high hardness, work hardening effect is remarkable, 304 stainless steel plate bending when the following features: because of poor thermal conductivity than ordinary low-carbon steel, low elongation, resulting in deformation force required; stainless steel sheet metal bending when compared with carbon steel have a strong tendency to rebound; stainless steel plate with respect to the steel due to the low elongation, the bending angle of the workpiece during bending R is greater than steel, or there may be cracks; Since 304 stainless steel with high hardness, work hardening effect significant in the choice of bending tool to select heat treatment hardness should reach more than 60HRC tool steel, carbon steel surface roughness than an order of magnitude bending tool.

    According to the above features, in general: the next unit size, thicker plates, the greater the force required to bend, and with increasing thickness bending force in the selection of the bending device should be larger margin; lower unit size , tensile strength, the smaller the elongation, the greater the force required to bend, bend angle should be greater.

According to the actual situation, to expand the size of a bend at right angles to the side of the workpiece minus the sum of two thickness, the design can meet the accuracy requirements, expand the amount calculated according to the empirical formula to simplify the calculation process greatly improve production efficiency; the higher yield strength material , the greater the amount of spring back, in order to obtain the bending member 90 degree angle, the smaller the pressure required for the knife angle will design. With respect to the same thickness of 304 stainless steel plate bending angle is large, it should pay special attention there would be bending crack, impact strength of the workpiece. No non-member is not the time to pull the light generated by the punch immediately outside back, sometimes in deep drawing non-touch play or vibration to Mongolia static hair cooked; also sometimes deep drawing first time after a period of storage or in use before the onset of the process.