Effect of Cr, Si, Al of stainless steel

    Cr, Si, Al is the F-forming element, is the main alloying element of stainless steel to obtain corrosion resistance.

    Cr stainless steel surface to form a dense (FeCr) 2O3, since the strong chemical stability and passivation of stainless steel is improved. Si, Al also played the same role, but the Si content is too high, it will cause a decline in the mechanical properties of stainless steel, and weldability decrease. Al is mainly used precipitation hardening stainless steel, grain refinement, solid solution strengthening effect; to increase the strength of steel at room temperature and high temperatures.

    Effect of Ni of stainless steel

    Ni is to expand the A element, when large to 9% Ni can be obtained A stable organization. Ni to make stainless steel surface passivation, expand steel in acid passivation range. A Ni alone to get the required number of large, usually used in conjunction with the Cr element.

    Effect of Mo and Cu to stainless steel

    Mo is the F-forming element. Mo stainless steel by adding the following effects: 1. steel improve stability in a non-oxidizing medium. 2. Cl ion generating pitting corrosion resistance. 3. A steel improve heat resistance. Because the F of dollars, when added Mo, Ni content shall be increased in order to maintain full steel A. Mo increases will reduce A stainless steel toughness.

    Cu can improve the non-oxidizing medium corrosion resistance of steel. Cr-Ni stainless steel will produce added Cu diffusion hardened structure, improve the heat resistance of steel.

    Effect of Ti and Nb on stainless steel

    Ti and Nb C is greater than the affinity of Cr, which can preferentially form stable carbides, lower tendency to intergranular corrosion. In the Cr-Ni stainless steel, Ti is generally added in an amount greater than 5 times of C, and the addition amount of Nb is generally greater than 8 times the C, and can make the most of C forms carbides to prevent the formation of Cr23C6, thereby reducing the Cr-depleted zone existence. For example: 321 Ti, the 347 Nb. Their intergranular corrosion tendency of less than 304.

    Effect of S and P on stainless steel

    It belongs to harmful elements, generally the lower the better. Since the desulfurization, dephosphorization there are some contradictions, while reducing S, P has been difficult. Currently S content of stainless steel are relatively low, and high P content.

    Effect of c of stainless steel

    C is A forming elements, can also improve the strength of steel, but the corrosion resistance negatively. Because the combination of C and Cr will cause the grain boundary Cr-depleted layer. It will result in increased C weldability decrease. Stainless steel C content in general control of 0.08%, for the amount of C is less than 0.03% of the suffix L logo.

Effect of alloying elements on stainless steel varies, when adding a number of elements, their role is not a simple superposition or offset, as sometimes happens new physical chemistry between them with each other.